Standard
Number
|
Description
|
Notes
|
BAMR
Products
|
Date
|
| ASTM
A153 |
Specification
for Zinc Coating (Hot-Dip) on Iron and Steel Hardware |
|
|
|
| ASTM
A525 |
Specification
for General Requirements for Steel Sheet, Zinc-coated (Galvanised)
by the Hot-Dip Process |
Galvanising |
|
|
| ASTM
B244 |
Measurement
of thickness of anodic coatings on aluminum and of other nonconductive
coatings on nonmagnetic basis metals with eddy-current instruments |
For
thin coatings, uncertainty to be less than 0.5 mic. Base properties
and thickness, edges, curvature, roughness, pressure, cleanliness.
Calibration with foils. |
|
1979
|
| ASTM
B499 |
Test
Method for Measurement of Coating Thicknesses by the Magnetic Method:
Nonmagnetic Coatings on Magnetic Basis Metals |
Coating
thickness, base properties and thickness, edges, curvature, direction
of working, residual magnetism, stray fields, coating conductivity,
probe orientation. Appendix: rough surfaces affect reading. |
|
1988
|
| ASTM
B659 |
Guide
for measuring thickness of metallic and inorganic coatings |
Magnetic,
eddy-current, XRF, beta, coulometric, microscope, gravimetric. |
|
1990
|
| ASTM
C321 |
Bond
strength of chemical-resistant mortars |
Use
a 50mm diameter dolly. |
|
|
| ASTM
C584 |
Test
Method for 60-deg. Specular Gloss of Glazed Ceramic Whitewares and
Related Products |
|
|
|
| ASTM
D 1186-B |
Nondestructive
measurement of dry film thickness of nonmagnetic coatings appied
to a ferrous base |
Method
B. Magnetic flux. Calibration, use, precision. |
|
1987
|
| ASTM
D 4787 |
Continuity
verification of liquid or sheet linings applied to concrete substrates |
High
voltage (above 900V) ac or dc test. Set voltage below dielectric
breakdown strength of lining.Move probe 1 ft/s (0.3 m/s) max. |
|
1988
|
| ASTM
D 5179 |
Measuring
Adhesion of Organic Coatings to Plastic Substrates by Direct Tensile
Testing |
Measuring
the force to remove a plastic stub from the surface. The stud to
be 25mm diam. Pull with a tensile tester. |
|
1991
|
| ASTM
D1186-A |
Nondestructive
measurement of dry film thickness of nonmagnetic coatings appied
to a ferrous base |
Method
A. Magnet, spring and scale. Calibration, use on dry films, precision. |
|
1987
|
| ASTM
D1212-A |
Measurement
of wet film thickness of organic coatings |
Method
A. Two concentric wheels with eccentric wheel in centre. Use on
wet films.Interchemical gauge specified so Elco 120 cannot claim
conformance. |
|
1985
|
| ASTM
D1400 |
Non-destructive
measurement of dry film thickness of non-conductive coatings applied
to a non-ferrous metal base |
Eddy
current probe and scale. Calibration, use on dry films, precision. |
|
1994
|
| ASTM
D1455 |
Test
Method for 60-deg. Specular Gloss of Emulsion Floor Polish |
|
|
|
| ASTM
D2200 |
Pictorial
Surface Preparation Standards for Painting Steel |
Method
A is ISO/Swedish, Method B is SSPC photographs and description. |
|
|
| ASTM
D2457 |
Test
Method for Specular Gloss of Plastic Films and Solid Plastics |
|
|
|
| ASTM
D3002 |
Practice
for Evaluation of Coatings for Plastics |
For
coatings on plastics. |
|
|
| ASTM
D3359 |
Measuring
Adhesion by Tape Test |
Method
A is X-cut and tape, Method B is latice pattern and tape. |
|
1987
|
| ASTM
D3359-B |
Measuring
adhesion by tape test |
Tool
and tape. Use 1mm for coatings upto 2.0 mils, 50 mic, and 2mm for
2 to 5, 50 to 125 mic. Classification of result. |
|
1987
|
| ASTM
D4138 |
Test
Method for Measurement of Dry Film Thickness of Protective Coating
Systems by Destructive Means |
|
|
|
| ASTM
D4414-A |
Measurement
of wet film thickness by notch gages |
Notched
steel or aluminium gauge. Use. |
|
1984
|
| ASTM
D4417-A |
Field
measurement of surface profile of blast cleaned steel |
Method
A. Profile comparator like Keane-Tator and Clemtex. With or without
magnification. |
|
1984
|
| ASTM
D4417-B |
Field
measurement of surface profile of blast cleaned steel |
Dial
gauge with 60 deg cone and 50 mic tip. Elco 123. Zero on glass. |
|
1984
|
| ASTM
D4417-C |
Field
measurement of surface profile of blast cleaned steel |
Replica
tape and micrometer. Testex tape and Mitutoyo 7326 micrometer. |
|
1984
|
| ASTM
D4541 |
Pull-off
strength of coatings using portable adhesion testers |
Pull-off
adhesion tester. Preparation, use and interpretation of result.
Annex A shows Model 106 and PATTI tester. |
|
1985
|
| ASTM
D523 |
Standard
test method for specular gloss |
Glossmeter
60, 20 or 85 deg. and standards. Calibration and use. |
|
1989
|
| ASTM
E337-B |
Measuring
humidity with a psychrometer (the measurement of wet- and dry-bulb
temperatures) |
Method
B - Psychrometer ventillated by whirling (sling psychrometer). Mercury
in glass thermometers. Use and calculations. |
|
1984
|
| ASTM
E376 |
Measuring
coating thickness by magnetic field or eddy-current (electromagnetic)
test methods. |
Coating
on metal substrate. Interferences: thick of coating, mag properties
of base, thick of base, structure and composition, edge effect,
curvature, smoothness, direction of rolling, residual magnetism,
stray mag fields, cleanliness, probe press & postn |
|
1989
|
| ASTM
G 6 |
Abrasion
resistance of pipeline coatings |
Porosity
test prior to test for abrasion resistance of pipeline coatings.
Low voltage (67.5V) and high voltage methods 1250.SQR(thou). |
|
1983
|
| ASTM
G12 |
Nondestructive
measurement of film thickness of pipeline coatings on steel |
Dry
films, up to 6mm, on steel pipe above 10mm . Magnetic thickness
gauge. Make 3 readings along the top edge and repeat every 90 deg.
Record min, max and mean. |
|
1983
|
| ASTM
G62-A |
Holiday
detection in pipeline coatings |
Method
A. Voltage less than 100 V dc. Alarm sounds at test resistance of
100 kOhm or less. Coating thickness below 0.508 mm.Use tap water
for below 0.254 mm, add wetting agent above this. |
|
1987
|
| ASTM
G62-B |
Holiday
detection in pipeline coatings |
Method
B. Pinholes, voids & thin spots in pipeline coatings. Holiday
detector. Use.Thickness less than 1.016mm, V = 3294 x SQR(T mm)
Thickness more than 1.041mm, V = 7843 x SQR(T mm) |
|
1987
|